Studies an oil-absorbing and room-temperature quick-curing adhesive.
研究了一种具有吸油性能的并且在常温下能够迅速凝胶固化的胶粘剂。
Influential factors on apparent density and oil absorbency of suspension resin;
影响悬浮树脂表观密度和吸油率的因素
The effects of the raw material ingredient, the amount of the dispersing agent, and the amount of the initiator on oil absorbency and gel fraction were investigated, and the optim.
重点研究了原料配比、引发剂用量、交联剂用量对树脂吸油率、凝胶量等性能的影响及规律，从而确定了最佳的实验条件。
Study on preparing ecotype oil sorbent material from wood fiber;
生态型木纤维吸油材料的制备与研究
A new type woody fiber oil sorbent material was prepared by pyrolysis of Fir TMP,the relation between oil absorption ability of the pyrolyzed TMP and pyrolysis temperature and extractives contents were studied.
将杉木TMP进行热解,制备出了新型木质纤维吸油材料。
During the production process of porous starch, oil adsorption ratio was used as an index toevaluate the porous starch.
工艺研究中,首先确定以吸油率作为衡量淀粉成孔的指标。
The NR oil absorption composites were prepared by using the stearic methacrylate-butyl acrylate-styrene(SMA-BA-St) copolymer as oil absorbent and NR grafted copolymer as compatibilizer,and its properties were investigated.
以甲基丙烯酸十八酯-丙烯酸丁酯-苯乙烯(SMA-BA-St)共聚物作吸油剂、NR接枝共聚物作相容剂制备NR吸油材料并对其性能进行研究。
The oil-absorption resins are prepared by suspension copolymerization of monomer butyl methacrylate and butyl acrylate,with N,N′-methylene bisacrylamide as crosslinking agent,benzoyl peroxide as initiator,polyvinyl alcohol as dispersing agent and water as disperal phase in this paper.
以甲基丙烯酸丁酯(BMA)和丙烯酸丁酯(BA)为单体、N,N′-亚甲基双丙烯酰胺为交联剂、过氧化苯甲酰为引发剂、聚乙烯醇为分散剂、水为分散介质,采用悬浮聚合法制备了自溶胀型的吸油树脂,并通过正交实验考察了交联剂、致孔剂对树脂吸油性能的影响。
The results showed that oil-absorption resin had better oil absorption rate after melting agent extraction when adding melting porogenic agent,which approved the dependent of oil-absorption resin to pole structure of resin.
本研究采用悬浮聚合法制备了致孔性丙烯酸酯吸油树脂。