The effectivity of controling hydrogen embrittlement by the inhibitor and the possibility of predicting hydrogen embrittlement through electrochemical polarization method were discussed.
研究了AHC-1及AHC-5两种飞机表面水基清洗剂对飞机表面典型金属材料的腐蚀性能及高强度钢氢脆性能的影响,探讨了应用缓蚀剂控制高强度钢氢脆的有效性以及用电化学极化法预测高强度钢在清洗剂中的氢脆倾向性。
The stress corrosion-induced cracking(SCC) of 20 steel in saturated H2S solution and its protection were studied using electrochemical polarization,slow strain rate tensile test and applied potential methods.
采用电化学极化、慢应变拉伸、外加极化电位等方法对20钢在饱和H2S溶液中的应力腐蚀及其预防措施进行了研究。
The mechanisms of the stearamide derivative inhibited CO2 corrosion on the mild steel X65 were studied in derivative containing aerated brine solution by electrochemical polarization measurements and electrochemical impedance spectroscopy (EIS) measurements.
通过电化学极化及电化学阻抗谱(EIS)测试研究了一种脂肪酰胺类缓蚀剂对X65低碳钢抗CO2腐蚀的机理,结果表明,该类缓蚀剂是一种阳极型缓蚀剂,属于界面吸附型,通过负催化机制产生缓蚀作用,对X65低碳钢抗CO2腐蚀具有良好的效果,其缓蚀效率随浓度的增加而提高,存在极值现象,在0。