Solid state polymer electrolyte film with room temperature conductivityof 5×10~(-3)s/cm is prepared by casting method at speific condition and itsX-ray diffraction patterns is made.
在一定条件下,用浇注法成功地制备出室温电导率为5×10~(-3)s/cm的固态聚合物薄膜电解质,并进行X射线粉末衍射谱分析,结果表明薄膜是非晶态结构。
ZrO_2/Ni functionally graded materials was fabricated via slip-casting under a gradient magnetic field(0.
根据不同组分的磁性差异,提出一种在梯度磁场中,采用粉浆浇注法制备铁磁性/非磁性功能梯度材料的方法,并用此方法制备出成分连续变化的ZrO_2/Ni功能梯度材料。
Sm and Gd co-doped CeO2 (SGC) powders were prepared by the gel-casting method.
通过凝胶浇注法制备了Sm,Gd共同掺杂的CeO2(SGC)粉末,将制得的粉末经1400℃高温烧结4h得到相应的SGC电解质烧结体,并对SGC粉末及相应的烧结体的性能进行了表征。
9(TiO2-SDC) powder was prepared from the corresponding nitrates and oxides by a gel-casting method.
以硝酸盐和氧化物为原料,通过凝胶浇注法制得了摩尔分数为10%TiO2-Ce0。