An in-depth study was conducted concerning the fusion temperature and fusion process dynamic characteristics of three representative pairs of ash samples taken from two units of coal water slurry (CWS)-fired boilers.
对取自2台水煤浆锅炉3对各具代表性灰的熔融温度和熔融过程动态特性进行了深入研究。
Plenty of medical glass bottles which were present in medical wastes had rather low fusion temperatures.
实验结果显示,不同化学组分对熔融温度有不同的影响,SiO2能够提高医用玻璃的熔融温度,B2O3和碱金属氧化物(Na2O、K2O)会大幅降低医用玻璃的熔融温度,而碱土金属氧化物(CaO、BaO)和Al2O3会使医用玻璃的软化温度升高,却能使流动温度降低。
The melting characteristics and behavior of heavy metals of fly ashes were investigated under different melting temperatures.
对城市垃圾与煤混烧飞灰进行旋风熔融试验,分析了不同熔融温度条件下熔渣的微观形貌及重金属行为。
The influence of fly ash on partition characteristics of heavy metals before and after melting treatment was studied , including the melting temperature, melting time and the basicity.
研究探讨了熔融温度、熔融时间、碱基度对飞灰熔融处理前后重金属分布特性的影响。
The melting temperature,melting heat,static and dynamic mechanical properties of PA6/PTFE blends and PA66/PTFE blends are experimentally investigated in this paper.
PA6/PTFE共混物的熔融温度随PTFE含量的增加而升高,熔融热却随PTFE含量的增加而降低。
As irradiation dose increases, the gel content and charpy impact strength increases, whereas crystallinity, melting point and elongation at break decreases.
结果表明 :在 0～ 30 0 k Gy的辐射剂量范围内 ,限定量的氧对 HDPE的性能并无太大的影响 ,HDPE的凝胶含量和缺口冲击强度随辐射剂量的增加而增加 ,但结晶度、熔融温度和断裂伸长率却随剂量的增加而下降。
By co polymerization between a flexible co-monomer and acrylonitrile reduces the melting point or increases the decomposition temperature in order to produce melt processable resin.
8℃,而熔融温度仅为188。
The mechanism of reducting of ash fusion temperature by adding flux in Huainan coal to reduce the ash fusion temperature,so that the coal can meet the temperature request of the slag-tap technology of Texaco CWM gasification device which has been introduced to Huainan Chemical Group in recent years,and the mechanism was studied in this paper.
添加助熔剂A降低高灰熔融性淮南煤灰熔融温度,使其适合淮化集团近年引入的Texaco水煤浆气化炉的液态排渣工艺温度要求(1 380℃左右),并对其机理进行了初步的探究。
Study on Improving the Fusibility of Shenhua-coal-ash;
提高神华煤灰熔融温度和熔融性的研究
Melting temperature distribution characteristic of ash deposits of black liquor coal slurry on furnace wall
黑液水煤浆炉壁灰沉积物熔融温度分布特性
Influence of Additives on Vitrified Bond Melting Temperature of CBN High-speed Grinding Tool
添加剂对CBN高速磨削工具用陶瓷结合剂熔融温度的影响
The yield, molecular weight, polar comonomer content and melting temperature of the poly(olefin-ester)s can be controlled by the change of polymerization reaction condition.
改变聚合条件，可控制烯烃共聚酯的分子量、极性单体插入率和熔融温度等性质。
DEVELOPMENT OF IDENTIFYING SOFTWARE FOR FUSIBILITY OF COAL ASH BY USING Visual C++
用Visual C++开发煤灰熔融特征温度识别软件
The Numerical Simulation for Temperature Field of MCFC Stack;
熔融碳酸盐燃料电池堆温度场的数值模拟
Tests of Homogenization Temperature and Volatile Content of Melt Inclusions
熔融包裹体均一温度及挥发组分含量测试
Analysis on factors influencing the accurate determination of coal ash fusibility temperature
准确测定煤灰熔融性温度的影响因素分析
The key points are caloric value of coal, the fusing characteristics of coal ash and the temperature at furnace center.
其要点是煤的热值，煤灰的熔融特性以及炉膛的中心温度。
Manufacture and Properties of Melt-Spun Heat-storage and Thermo-regulated Fiber Containing Microencapsulated Phase Change Materials;
熔融纺丝法智能温度调节纤维的研制与性能分析
Rapid growth of“ mother dendrites” in a given location of a melt at just below the liquidus temperature, that growth being the result of rapid heat extraction from the melt, or from recalescence.
在特定的熔点，以低于液相线的温度快速生成“母晶枝”，这是使熔融金属或复辉快速散热的结果。
melting point type disposable fever thermometer
熔点型消耗式温度计
fusible-element-type fixed temperature detector
易熔合金温度探测器
Now, the consumptive optical fiber radiation thermometer developing is a new method of the temperature measurement for melted metal.
现在，开发的消耗型光纤辐射温度计是一种全新的测量熔融金属温度的方法。
Equilibrium Comparison
金属的相融、相融温度、晶体反应及合金在共晶合金、固熔孻共晶合金及偏晶反应的比较
For example, a variation of20% in the feed rate causes a9% increase or decrease in pressure, which is a variability range of18%.
温度恒定时，熔融粘度变化通常是由于投料速率变化和/或混和不均导致的。
The warm-up device can reduce the temperature difference between the cloth and the molten film, so it improve the intensity of antis tripping, reduce the gaffer of the film.
预热装置缩小了材料和熔融薄膜的温度差，保证了涂覆后抗剥离强度高，减轻涂覆后的皱褶。
The addition of a plasticizer may lower the melt viscosity, elastic modulus, and glass transition temperature (Tg) of a plastic.
同时,加入增塑剂,还可以降低塑料在熔融态时的粘度、弹性模数及玻璃转变温度(tg)。