Development of Ti pigments used in cosmetics abroad;
国外化妆品用钛系颜料的开发进展
Recent research progress of synthesis methods and technologies of titanium yellow pigments are introduced,in terms of the preparation methods of nano-materials.
结合纳米材料的制备方法,概述了钛黄颜料制备方法及工艺,主要有固相反应法和液相反应法。
In this paper, titanium-nickel yellow pigments were prepared by homogenous precipitation method and Sol-Gel method.
本文采用均匀沉淀法和溶胶-凝胶法制备了钛镍黄颜料,并在均匀沉淀法的基础上,加入不同的矿化剂制备复合型钛镍黄颜料。
The surface of TiO 2 pigment particles are modified to improve the dispersion stability of the TiO 2 pigment in paint.
通过对二氧化钛颜料颗粒进行表面有机改性以提高其在油漆中的分散性 ,研究了表面改性剂及用量对颜料分散性的影响。
SURFACE TREATMENT OF TiO_2 PIGMENT FOR MATT EMULSION COATINGS
平光乳胶漆用二氧化钛颜料的表面处理
Typical material is phosphor, titanium pigment and kinds of high purity pigment.
典型的物料有荧光粉、钛白粉和各种高纯颜料等。
Purpose -To synthesise calcium titanate with a perovkite structure as an anticorrosion pigment for metal protecting paints.
目的-采用具钙钛矿结构的钛酸钙合成用于金属保护漆的防腐颜料。
Study on Preparation of Serial Iron Oxide Pigments from By-product of TiO_2-ferrous Sulfate;
钛白副产硫酸亚铁制备氧化铁系列颜料的研究
Current Research and Recent Development of Mica Titania Pearlescent Pigments;
云母钛珠光颜料的研究现状及发展方向
The Research of Perovskite-Type YAl_((1-x))Cr_xO_3 Ceramic Red Pigment
钙钛矿型YAl_((1-x))Cr_xO_3红色陶瓷颜料的研究
RESEARCH PROGRESS OF PREPARATION AND INFLUENCE FACTORS ON APPLICATION PERFORMANCE OF TITANIUM YELLOW PIGMENT
钛黄颜料的制备及其性能影响因素的研究进展
Why add phosphoric acid in anatase titanium dioxide?
阐述了在生产锐钛型钛白粉颜料中,加入磷酸的目的、量、钛白粉的影响,以及加入磷酸的方法.
Findings -Calcium titanate was prepared from materials that do not add any impurities to the anticorrosion properties of the pigment.
发现-钛酸钙由不添加影响颜料防腐性能的任何杂质的材料制得。
The synthesised calcium titanate was used to prepare epoxy coatings with varying contents of the anticorrosion pigment.
合成的钛酸钙与不同含量的防腐颜料用于制备环氧树脂涂料。
Originality/value -The method of synthesising calcium titanate as an anticorrosion pigment is new.
新型/价值-采用钛酸钙合成防腐颜料的方法乃新型方法。
Study on the Preparation of Titanium Dioxide Compound Pigments Based on Kaolin Substrates;
以高岭土为基材制备二氧化钛复合颜料试验研究
Study on the craft of preparing iron oxide pigment from by-product of TiO_2--ferrous sulfate;
钛白副产硫酸亚铁制备氧化铁系颜料工艺的研究
Surface Characteristics and Preparatory Conditions of the Titania-mica Pearlescent Pigment;
云母钛珠光颜料表面形貌的研究与制备条件的控制
It was identified that calcium titanate of perovskite structure is a highly efficient anticorrosion pigment for paints.
结果发现具钙钛矿结构的钛酸钙是一种适用于油漆的高效防腐颜料。
A pigment or dye having this hue.
黄色颜料，黄色染料具有这种颜色的颜料或染料
raw sienna,ie brownish-yellow
生赭石（棕黄颜料）.
burnt sienna, ie reddish-brown
赭石（赤褐色颜料）